Use of positron annihilation measurements to detect the defect beneath worn surface of stainless steel 1.4301 (EN) under dry sliding condition
2012
Abstract Positron measurements were performed for detection of the subsurface zone in the stainless steel 1.4301 (EN) exposed to dry sliding. They revealed the defect profile induced by dry sliding which is extended inward the worn surface from 85 μm to 400 μm depending on the applied load during the tribo-test. This result was obtained using the positron techniques, while the microhardness profile exhibited shorter range of the microhardness depth profile, i.e., from 70 μm to 150 μm. However, at the depth of about 5 μm from the worn surface the sudden increase in the microhardness was observed. The complementary measurements of X-ray diffraction and SEM micrographs of the worn surface were…
Recrystallization in subsurface zone seen by positron annihilation
2010
Abstract The paper presents studies of the defect distribution, detected by the positron annihilation method in the subsurface zone (SZ) of copper samples after dry sliding wear. It takes advantage of a new experimental technique based on scanning of the positron implantation profile. It allowed us to detect the defect profile in copper to the depth of 200 μm in a nondestructive way and study isochronal annealing behavior of this profile. We determined that annealing induces a recrystallization process which runs faster close to the surface than in deeper regions. After sliding, the complete recrystallization of the substructure takes place at temperature c.a. 600 °C. Some changes in the de…